Meiah 高活性三元乙丙超细交联橡胶
Meiah-E-1
产品特性
三元乙丙超细交联橡胶在三元乙丙中的基础试验分析 |
材料名称 |
基本配合 |
1 |
EPDM4640 |
100 |
100 |
100 |
100 |
100 |
2 |
ZnO |
5 |
5 |
5 |
5 |
5 |
3 |
SA |
1 |
1 |
1 |
1 |
1 |
4 |
N550 |
110 |
110 |
110 |
110 |
110 |
5 |
N330 |
34 |
34 |
34 |
34 |
34 |
6 |
TUDALEN11(石蜡油) |
30 |
30 |
30 |
30 |
30 |
7 |
|
|
|
|
|
|
8 |
EPDM粉 |
0 |
20 |
30 |
50 |
100 |
9 |
BZ |
1 |
1 |
1 |
1 |
1 |
10 |
DM |
1 |
1 |
1 |
1 |
1 |
11 |
TT |
0.5 |
0.5 |
0.5 |
0.5 |
0.5 |
12 |
S |
1 |
1 |
1 |
1 |
1 |
|
|
|
|
|
|
|
13 |
合计 |
283.5 |
303.5 |
313.5 |
333.5 |
383.5 |
物理性能 |
0 phr |
20 phr |
30 phr |
50 phr |
100 phr |
1 |
180℃×8′硫化仪 |
|
|
|
|
|
|
ML(N.M) |
0.46 |
0.48 |
0.5 |
0.5 |
0.55 |
|
MH(N.M) |
3.27 |
2.92 |
2.82 |
2.65 |
2.33 |
|
T10 |
52″ |
52″ |
52″ |
49″ |
47″ |
|
T90 |
4′06″ |
3′58″ |
4′01″ |
3′58″ |
3′34″ |
|
|
|
|
|
|
|
2 |
基本物性 |
硫化条件180℃×8′ |
|
|
|
|
硬度,shore A,GB/T531 |
80 |
79 |
79 |
79 |
79 |
|
扯断强度,Mpa,GB/T528 |
8.03 |
8.32 |
8.53 |
8.25 |
8.55 |
|
扯断伸长率,%,GB/T528 |
203.47% |
229% |
254.72% |
239.12 |
252.61 |
|
|
|
|
|
|
|
3 |
热空气老化120℃×70h,GB/T3512 |
|
硬度,shore A |
+4 |
+5 |
+6 |
+5 |
+5 |
|
强度变化率,% |
8.97% |
8.05% |
7.62% |
6.67% |
2.22% |
|
扯断伸长率变化率,% |
-24.76% |
-31.49% |
-37.75% |
-34.04% |
-34.89% |
备注:以上技术资料仅供参考,不做规格指标之用. |
炼胶工艺:生胶与超细交联橡胶(低硬度胶料)一般不需要单独塑炼,稍加压合就可以开始混炼.辊距4--6mm,上胶左右倒胶均匀。当形成光滑连续包辊胶(应有适当堆积胶),其余炼胶工艺按常规。
产品优点
1.其生产原理为固相力化学常温力化学改性,使胶粉的比表面积得以增大,活性增强,提高了其与高分子材料的界面结合力,保证了产品的原性能基本不变;
2.本产品为高活性三元乙丙胶超细交联橡胶,其材料来源均为进口的胶边,其产品的来源相当的稳定。
3.本公司对来料进行严格的进料检验,并有专业系统的处理工序,对胶边的分级采取严格的检验控制;
4.一般精细胶粉的掺用量为10%以下,而本品经过改性,在原配方不变的情况下其掺用量可提高到25%~50%,对硫化橡胶的拉伸强度,伸长率,硬度,热氧老化等物理橡胶性能影响甚微,可大幅度降低三元乙丙混炼胶成本。
5.随着EPDM粉的增加,对耐臭氧性能影响甚微。
应用范围
密封条,胶管,胶板,水封,胶带等三元乙丙为主体材料的制品。
三元乙丙超微胶粉
原 材 料:汽车密封条残次品
形 状:黑色毛糙颗粒
处理工艺:常温下切割精磨
化学组成:乙丙橡胶、炭黑颗粒
技术指标:
名称 |
保证值 |
颜色 |
黑色 |
平均粒径um≤ |
150 |
过筛率≥ |
90% |
铁含量 |
0.003% |
纤维含量 |
0.3% |
拉伸强度,Mpa≥ |
8 |
扯断伸长率,%≥ |
300 |
硬度,±5 ShoreA |
65 |
基本配方:EPDM4640,100;氧化锌,5:硬脂酸,1;N330,34;石蜡油,10;三元乙丙超微胶粉,50;BZ,1;DM,1;;TT,0.5;S,1
用途:三元乙丙橡胶制品
包装:25kg/袋
储存:干燥环境,忌明火
产地:江苏丹阳